高文林,王向杰,李国爱,班春燕,陆政,崔建忠.-180℃深冷处理对7A99铝合金峰值时效强韧性能与析出行为的影响[J].稀有金属材料与工程(英文),2019,48(9):2937~2943.[Gao Wenlin,Wang Xiangjie,Chen Junzhou,Ban Chunyan,Lu Zheng and Cui Jianzhong.Effect of Deep Cryogenic Treatment of -180℃ on Strength and Toughness Properties and Precipitation Behavior of 7A99 Aluminium Alloy[J].Rare Metal Materials and Engineering,2019,48(9):2937~2943.]
Effect of Deep Cryogenic Treatment of -180℃ on Strength and Toughness Properties and Precipitation Behavior of 7A99 Aluminium Alloy
Download Pdf??View/Add Comment??Download reader
Received:March 21, 2018??Revised:April 28, 2018
DOI:
Key words:?-180℃ deep cryogenic treatment??7A99 aluminium alloy??3DAP??precipitation behavior??strength and toughness properties
Foundation item:国家重点研发计划(2016YFB0300901),国家自然科学基金:(U1608252、U1708251、51574075)
Author NameAffiliation
Gao Wenlin,Wang Xiangjie,Chen Junzhou,Ban Chunyan,Lu Zheng and Cui Jianzhong??
Hits:?28
Download times:?3
Abstract:
??????Indirect extrusion of 7A99 ultrahigh-strength aluminium alloy was heat treated by T6 peak aging treatment and peak cold-heat cycle aging treatment of -180℃ (T6-DCT). XRD, TEM, HRTEM and 3DAP were applied to study the influences of T6-DCT treatment on the strength and toughness properties, precipitation behavior. The result shows that The lattice constant of Al matrix increases from 0.40551 nm to 0.40626 nm after T6-DCT, which plays a solid solution strengthening role. A large number of η phase generate in the grains, and the η phases at the grain boundaries are discontinuous, meanwhile the precipitation free zone is formed at the grain boundaries, which reduces the tensile strength. After T6-DCT treatment, the segreation degree of Zn and Mg increases, the precipitation ratio and distribution uniformity of precipitated phases decrease. The avearge equivalent radius of the precipitated phases changes from 1.2 nm to 1.14 nm after T6-DCT treatment, the density of the precipitated phases decrease from 4.53×1024/m3 to 3.87×1024/m3, which weaken the precipitation-strengthening. The strength and toughness improve significantly after T6-DCT treatment, which shows that the strength is slightly reduced and the toughness is improved remarkably.