邹东利,陈向林,肖大武,何立峰,帅茂兵,李玉斌.5A06铝合金激光焊接接头显微组织及力学性能研究[J].稀有金属材料与工程(英文),2019,48(9):2951~2956.[Zou Dongli,Chen Xianglin,Xiao Dawu,He Lifeng,Shuai Maobing and Li Yubin.Microstructure and mechanical properties of 5A06 aluminium alloy laser welded joint[J].Rare Metal Materials and Engineering,2019,48(9):2951~2956.]
Microstructure and mechanical properties of 5A06 aluminium alloy laser welded joint
Download Pdf??View/Add Comment??Download reader
Received:April 17, 2018??Revised:June 05, 2018
DOI:
Key words:?aluminium alloy??laser welding??microstructure??mechanical property
Foundation item:国家重点研发计划(2016YFB1102104-4),国家自然科学(51401187)
Author NameAffiliation
Zou Dongli,Chen Xianglin,Xiao Dawu,He Lifeng,Shuai Maobing and Li Yubin??
Hits:?23
Download times:?9
Abstract:
??????The microstructure and mechanical properties of 5A06 aluminium alloy laser welded joint with thickness of 30 mm were investigated in this paper. The experimental results show that an amount of pore defects were found in weld seam zone, and the welded defects were mainly located at the grain boundary. The proportion of the welded defects with size less than 100 μm was beyond 50%. The microstructure in weld seam zone was mainly composed of dendritic grians, and several dendritic grians were located in a single grains. The misorientation between the dendritic grians was less than 5o, and the contrast between the dendritic grians was caused by element Mg microsegregation. The obvious interface was observed between the weld seam zone and heat-affected zone, and the contents of low angle boundary in heat-affected zone were higher than that of weld seam zone. Meanwhile, the grain morphology and size in heat-affected zone were different from the weld seam zone. Microhardness measurement shows that the definitive fluctuation of microhardness values in weld seam zone was observed, and the microhardness values of weld seam zone were beyond that of the microhardness values of matrx.