何波,雷涛,孙长青,杨光.激光沉积TC4/TC11梯度材料组织与疲劳性能研究[J].稀有金属材料与工程(英文),2019,48(9):3048~3054.[He Bo,Lei Tao,Sun Changqing and Yang Guang.Microstructure and fatigue properties of TC4/TC11 gradient materials by laser deposition[J].Rare Metal Materials and Engineering,2019,48(9):3048~3054.]
Microstructure and fatigue properties of TC4/TC11 gradient materials by laser deposition
Download Pdf??View/Add Comment??Download reader
Received:April 17, 2018??Revised:June 03, 2018
DOI:
Key words:?laser deposition manufacturing??titanium alloy??gradient materials??microstructure??fatigue properties
Foundation item:国家重点研发计划项目(2017YFB1104002);工信部民用飞机专项科研项目(MJZ-2016-G-71);辽宁省教育厅科学研究项目(L201738和LQN201722),航空制造工艺数字化国防重点学科实验室开放基金(SHSYS2017007)
Author NameAffiliation
He Bo,Lei Tao,Sun Changqing and Yang Guang??
Hits:?27
Download times:?6
Abstract:
??????In order to study the microstructure and fatigue properties of laser deposited TC4/TC11 gradient materials, directly transited and gradiently transited TC4/TC11 composite materials were prepared by laser deposition manufacturing technology. The microstructures of composite materials by different transition were observed, the fatigue properties of these two composite materials under stresses of 550 MPa and 800 MPa were tested, and fatigue fractures were analyzed. The results show that the interface of the microstructure of the gradient material with 3 transition layers is not obvious, and microstructures of TC4 and TC11 are integrated more tightly in the transition zone than that of the directly transition composite materials. The fatigue life of the gradient material with 3 transition layers under either stress is higher than that of the direct transition, which is relatively increased by 129.3% under low stress and 81.8% under high stress. The direct transition composite material cracks along the bunch of α-sheet during crack propagation, with a large sliding surface and a low fatigue life. The cracks of gradient material with 3 transition layers grow along a single α-sheet, the slip plane is small, and the crack propagation path is more tortuous, which improves the fatigue life.