李萍,吴广善,魏学峰,王薄笑天,严思梁,薛克敏.高压扭转对Al-Zn-Mg-Cu-Zr合金抗应力腐蚀性能影响[J].稀有金属材料与工程(英文),2019,48(9):2981~2986.[Li Ping,Wu Guangshan,Wei Xuefeng,Wang Boxiaotain,Yan Siliang and Xue Kemin.Effect of high pressure torsion on stress corrosion resistance of Al-Zn-Mg-Cu-Zr aluminum alloy[J].Rare Metal Materials and Engineering,2019,48(9):2981~2986.]
Effect of high pressure torsion on stress corrosion resistance of Al-Zn-Mg-Cu-Zr aluminum alloy
Download Pdf??View/Add Comment??Download reader
Received:May 24, 2018??Revised:June 23, 2018
DOI:
Key words:?Al-Zn-Mg-Cu-Zr aluminium alloy??high pressure torsion??electrochemical corrosion??stress corrosion resistance
Foundation item:国家自然科学基金项目(面上项目,重点项目,重大项目)
Author NameAffiliation
Li Ping,Wu Guangshan,Wei Xuefeng,Wang Boxiaotain,Yan Siliang and Xue Kemin??
Hits:?28
Download times:?3
Abstract:
??????High pressure torsion (HPT) experiment followed with heat treatment were carried out on as-received Al-Zn-Mg-Cu-Zr alloy at 400 ℃ under the pressure of 1 GPa. Optical microscope, electrochemical workstation and slow strain rate tensile machine were used for microstructure observation, electrochemical corrosion and stress corrosion resistance test for the as-received and HPT processed samples respectively. The results show that HPT processing can improve the tensile strength and stress corrosion resistance by modifying the size and distribution of grains and second phases. The second phases agglomerated at the grain boundary corrode continuously, which leads to obvious intergranular corrosion and weak stress corrosion resistance of the as-received alloy. After 0.5 turn of HPT processing, the fragmentation and content reduction of second phase lead to the decrease of corrosion sensitivity, at the same time, the planar slip reduces and homogeneous slip mode increases due to grain refinement, which synthetically results in a significant improvement of the stress corrosion resistance. The HPT processed sample with 2 turns has finer grains with uniform distribution, which leads to the further increases of homogeneous slip mode compared with 0.5 turn, but under the interaction of intense pitting and stress concentration, the resistance to stress corrosion slightly decreases.