罗萃,邱小明,阮野,卢裕臻,邢飞.Zn基钎料钎焊烧结NdFeB与DP1180钢接头微观组织及性能[J].稀有金属材料与工程(英文),2019,48(9):2779~2784.[Luo Cui,Qiu Xiaoming,Ruan Ye,Lu Yuzhen and xingfei.Microstructure and properties of soldering sintered NdFeB permanent magnet to DP1180 steel using Zn-based alloy[J].Rare Metal Materials and Engineering,2019,48(9):2779~2784.]
Microstructure and properties of soldering sintered NdFeB permanent magnet to DP1180 steel using Zn-based alloy
Download Pdf??View/Add Comment??Download reader
Received:September 12, 2018??Revised:October 22, 2018
Key words:?Sintered NdFeB permanent magnet??Soldering??Microstructure??Magnetic properties??Shear strength
Foundation item:中国博士后科学基金
Author NameAffiliation
Luo Cui,Qiu Xiaoming,Ruan Ye,Lu Yuzhen and xingfei??
Download times:?4
??????In this work, sintered NdFeB permanent magnet (NdFeB) was firstly soldered with DP1180 steel using Zn-5Sn-2Cu-1.5Bi (ZSCB) solder. Soldering was performed in an inert atmosphere control high-frequency induction furnace, and then the microstructure, magnetic properties and shear strength were investigated by optical microscope, scanning electronic microscopy, energy dispersive X-ray analysis, NIM-2000H magnetic tester and mechanical testing machine. Results showed that the interface between NdFeB / ZSCB solder formed metallurgical bonding with Nd-Fe-Zn and Fe-Zn. FeZn13 and Fe3Zn10 phases formed in steel side of the joints. Besides, the soldering temperature had slight influence on the magnetic properties of NdFeB. Finally, compared with adhesive bonding in traditional method, the shear strength of the soldering joints were dramatically improved by 35.38%, from 32.50 MPa to 44.00 MPa. The shear strength was high enough to cause failure in NdFeB side of the joints. Fracture of the joints was caused by large difference thermal expansion coefficient between NdFeB and ZSCB solder as a result of high stress at the reaction layer closing to NdFeB.